PA 3200 GF

Material Data Sheet

PA 3200 GF

Product Description

PA 3200 GF is a white polyamide 12 powder filled with glass beads. Parts made from PA 3200 GF show high rigidity while maintaining a good elongation at break. In addition, they are characterized in particular by their special wear resistance, which makes them a perfect fit for increased abrasion resistance requirements.

MAIN CHARACTERISTICS

  • High stiffness
  • Wear resistance
  • Improved temperature performance

TYPICAL APPLICATIONS

  • Machine components that require enhanced siffness under load, e.g., housings
  • Heavily used parts that require enhanced wear and abrasion resistance
  • Forming tools
MECHANICAL PROPERTIES DRY / CONDITIONED UNIT TEST STANDARD
Tensile Modulus
X Orientation
Y Orientation
Z Orientation

3200 / -
3200 / -
2500 / -

MPa
MPa
MPa
ISO 527-1/-2
Tensile Strength
X Orientation
Y Orientation
Z Orientation

51 / -
51 / -
47 / -

MPa
MPa
MPa
ISO 527-1/-2
Strain at Break
X Orientation
Y Orientation
Z Orientation

9 / -
9 / -
5.5 / -

%
%
%
ISO 527-1/-2
Flexural Modulus
X Orientation

2900 / -

MPa
ISO 178
Flexural Strength
X Orientation

73 / -

-
ISO 178
Charpy Impact Strength (+23°C)
X Orientation

35 / -

kJ/m²
ISO 179
Charpy Notched Impact Strength (+23°C)
X Orientation

5.4 / -

kJ/m²
ISO 179
Izod Impact Strength (+23°C)
X Orientation

21 / -

kJ/m²
ISO 179
Izod Notched Impact Strength (+23°C)
X Orientation

4.2 / -

kJ/m²
ISO 179
Ball Indentation Hardness
X Orientation

98 / -

MPa
ISO 2039-1
Shore D Hardness
X Orientation

80 / -

-
ISO 7619-1
THERMAL PROPERTIES DRY / CONDITIONED UNIT TEST STANDARD
Melting Temperature - °C ISO 11357-1/-3
Temperature of Deflection under Load 1.80 MPa
X Orientation

96

°C
ISO 75-1/-2
Temperature of Deflection under Load 0.45 MPa
X Orientation

157

°C
ISO 75-1/-2
OTHER PROPERTIES VALUE UNIT TEST STANDARD
Density 1.22 g/cm³ EOS Method
Powder Color whitish - -
Components Color whitish - -