PA 2200 Top Speed

Material Data Sheet

PA 2200 Top Speed

Product Description

PA 2200, based on polyamide 12, offers a wide range of applications thanks to its very balanced property profile and is the most proven material on the market. 

PA 2200 is also available as the Responsible Product PA 2200 CarbonReduced. It combines a heavily reduced CO2e footprint with the well-known technical properties of PA 2200.

Top Speed, with 180 µm layer thickness, is a very economical parameter set for parts with medium to high requirements of quality and mechanical load and high cost pressure. Particularly large and relatively thick-walled parts can usually profit from this layer thickness, mostly without any noticeable impairment from the fast build-up rates.

MAIN CHARACTERISTICS

  • Balanced property profile
  • Multipurpose material

TYPICAL APPLICATIONS

  • Production equipment like grippers, jigs and fixtures
  • Surgery cutting guides and bone models for the medical industry
  • Eyewear in the consumer goods industry
  • Spare parts like brackets or covers, e.g., in the automotive industry
  • Functional parts for prototyping that include hinges or threads
MECHANICAL PROPERTIES DRY / CONDITIONED UNIT TEST STANDARD
Tensile Modulus
X Orientation
Y Orientation
Z Orientation

1500 / -
1500 / -
1500 / -

MPa
MPa
MPa
ISO 527-1/-2
Tensile Strength
X Orientation
Y Orientation
Z Orientation

45 / -
45 / -
38 / -

MPa
MPa
MPa
ISO 527-1/-2
Nominal Strain at Break
X Orientation
Y Orientation
Z Orientation

18 / -
18 / -
3 / -

%
%
%
ISO 527-1/-2
Shore D Hardness
X Orientation

75 / -

-
ISO 7619-1
OTHER PROPERTIES VALUE UNIT TEST STANDARD
Powder Color white - -
Components Color white - -