POLYMER SOLUTIONS
PA 2200 CarbonReduced Balance
Material Data Sheet
PA 2200 CarbonReduced Balance
Product Description
PA 2200 CarbonReduced, based on polyamide 12, offers a wide range of applications thanks to its very balanced property profile and is the most proven material on the market.
PA 2200 CarbonReduced is an EOS Responsible Product. It combines a heavily reduced CO2e footprint with the well-known technical properties of PA 2200.
The advantage of the process parameter Balance, at 120µm layer thickness, lies in its ability to balance different factors at the same time, e.g., production costs, mechanical properties, surface quality and accuracy. Therefore it is suitable for parts with varying geometries, dimensions and requirements.
- 100% proven quality and 45% less CO2e
- Balanced property profile
- Multipurpose material
- Production equipment like grippers, jigs and fixtures
- Surgery cutting guides and bone models for the medical industry
- Eyewear in the consumer goods industry
- Spare parts like brackets or covers, e.g., in the automotive industry
- Functional parts for prototyping that include hinges or threads
| MECHANICAL PROPERTIES | DRY / CONDITIONED | UNIT | TEST STANDARD |
|---|---|---|---|
|
Tensile Modulus X Orientation Y Orientation Z Orientation |
1650 / - 1650 / - 1650 / - |
MPa MPa MPa |
ISO 527-1/-2 |
|
Tensile Strength X Orientation Y Orientation Z Orientation |
48 / - 48 / - 42 / - |
MPa MPa MPa |
ISO 527-1/-2 |
|
Nominal Strain at Break X Orientation Y Orientation Z Orientation |
18 / - 18 / - 4 / - |
% % % |
ISO 527-1/-2 |
|
Flexural Modulus X Orientation |
1500 / - |
MPa |
ISO 178 |
|
Charpy Impact Strength (+23°C) X Orientation |
53 / - |
kJ/m² |
ISO 179/1eU |
|
Charpy Notched Impact Strength (+23°C) X Orientation |
4.8 / - |
kJ/m² |
ISO 179/1eA |
|
Izod Notched Impact Strength (+23°C) X Orientation |
4.4 / - |
kJ/m² |
ISO 180/1A |
|
Shore D Hardness X Orientation |
75 / - |
- |
ISO 7619-1 |
| THERMAL PROPERTIES | DRY / CONDITIONED | UNIT | TEST STANDARD |
|---|---|---|---|
| Melting Temperature | 176 | °C | ISO 11357-1/-3 |
|
Temperature of Deflection under Load 1.80 MPa X Orientation Z Orientation |
64 57 |
°C °C |
ISO 75-1/-2 |
|
Temperature of Deflection under Load 0.45 MPa X Orientation Z Orientation |
157 145 |
°C °C |
ISO 75-1/-2 |
|
Vicat Softening Temperature X Orientation |
176 |
°C |
ISO 306/B50 |
|
Burning Behavior, 0.50 mm nom. Thickness Thickness Tested |
HB 0.5 |
class mm |
UL 94 |
|
Burning Behavior, 1.60 mm nom. Thickness Thickness Tested |
HB 1.6 |
class mm |
UL 94 |
|
Burning Behavior, 3.2 mm nom. Thickness Thickness Tested |
HB 3.2 |
class mm |
UL 94 |
| ELECTRICAL PROPERTIES | DRY / CONDITIONED | UNIT | TEST STANDARD |
|---|---|---|---|
|
Comparative Tracking Index CTI X Orientation Y Orientation Z Orientation |
≥600 / - ≥600 / - ≥600 / - |
|
IEC 60112 |
| OTHER PROPERTIES | VALUE | UNIT | TEST STANDARD |
|---|---|---|---|
| Density | 0.93 | g/cm³ | EOS Method |
| Powder Color | white | - | - |
| Components Color | white | - | - |