3D printed spinal surgery parts  | © EOS & Anatomics
POLYMER SOLUTIONS

PA 2200 Balance

Material Data Sheet

PA 2200 Balance

Product Description

PA 2200, based on polyamide 12, offers a wide range of applications thanks to its very balanced property profile and is the most proven material on the market. 

PA 2200 is also available as the EOS Responsible Product PA 2200 CarbonReduced. It combines a heavily reduced CO2e footprint with the well-known technical properties of PA 2200.

The advantage of the process parameter Balance, at 120µm layer thickness, lies in its ability to balance different factors at the same time, e.g., production costs, mechanical properties, surface quality and accuracy. Therefore it is suitable for parts with varying geometries, dimensions and requirements.

MAIN CHARACTERISTICS

  • Balanced property profile
  • Multipurpose material

TYPICAL APPLICATIONS

  • Production equipment like grippers, jigs and fixtures
  • Surgery cutting guides and bone models for the medical industry
  • Eyewear in the consumer goods industry
  • Spare parts like brackets or covers, e.g., in the automotive industry
  • Functional parts for prototyping that include hinges or threads
MECHANICAL PROPERTIES DRY / CONDITIONED UNIT TEST STANDARD
Tensile Modulus
X Orientation
Y Orientation
Z Orientation

1650 / -
1650 / -
1650 / -

MPa
MPa
MPa
ISO 527-1/-2
Tensile Strength
X Orientation
Y Orientation
Z Orientation

48 / -
48 / -
42 / -

MPa
MPa
MPa
ISO 527-1/-2
Strain at Break
X Orientation
Y Orientation
Z Orientation

18 / -
18 / -
4 / -

%
%
%
ISO 527-1/-2
Flexural Modulus
X Orientation

1500 / -

MPa
ISO 178
Charpy Impact Strength (+23°C)
X Orientation

53 / -

kJ/m²
ISO 179/1eU
Charpy Notched Impact Strength (+23°C)
X Orientation

4.8 / -

kJ/m²
ISO 179/1eA
Izod Notched Impact Strength (+23°C)
X Orientation

4.4 / -

kJ/m²
ISO 180/1A
Shore D Hardness
X Orientation

75 / -

-
ISO 7619-1
THERMAL PROPERTIES DRY / CONDITIONED UNIT TEST STANDARD
Melting Temperature 176 °C ISO 11357-1/-3
Temperature of Deflection under Load 1.80 MPa
X Orientation
Z Orientation

64
57

°C
°C
ISO 75-1/-2
Temperature of Deflection under Load 0.45 MPa
X Orientation
Z Orientation

157
145

°C
°C
ISO 75-1/-2
Vicat Softening Temperature
X Orientation

176

°C
ISO 306/B50
Burning Behavior, 0.50 mm nom. Thickness
Thickness Tested
HB, Test passed
0.5
class
mm
UL 94
Burning Behavior, 1.60 mm nom. Thickness
Thickness Tested
HB, Test passed
1.6
class
mm
UL 94
Burning Behavior, 3.2 mm nom. Thickness
Thickness Tested
HB, Test passed
3.2
class
mm
UL 94
ELECTRICAL PROPERTIES DRY / CONDITIONED UNIT TEST STANDARD
Comparative Tracking Index CTI
X Orientation
Y Orientation
Z Orientation

≥600 / -
≥600 / -
≥600 / -



IEC 60112
OTHER PROPERTIES VALUE UNIT TEST STANDARD
Density 0.93 g/cm³ EOS Method
Powder Color white - -
Components Color white - -