Material Data Sheet

EOS NickelAlloy HAYNES® 282® is a precipitation strengthened nickel-base superalloy with a unique combination of high temperature strength, thermal stability, and fabricability. HAYNES® 282® alloy was developed for high temperature structural applications and is manufactured under license from Haynes International Inc. EOS NickelAlloy HAYNES® 282® is a nickel alloy powder intended for manufacturing parts on EOS metal systems with EOS DMLS processes.

MAIN CHARACTERISTICS

Excellent strength at high temperature
Good corrosion and oxidation resistance
Easily fabricated and excellent weldability

Download Process Data Sheet (PDF)

TYPICAL APPLICATIONS

Aerospace and rocket engine components
Turbomachinery and gas turbine parts
Energy industry components

The EOS Quality Triangle

EOS uses an approach that is unique in the AM industry, taking each of the three central technical elements of the production process into account: the system, the material and the process. The data resulting from each combination is assigned a Technology Readiness Level (TRL) which makes the expected performance and production capability of the solution transparent.

EOS incorporates these TRLs into the following two categories:

Premium products (TRL 7-9): offer highly validated data, proven capability and reproducible part properties.
Core products (TRL 3 and 5): enable early customer access to newest technology still under development and are therefore less mature with less data.

All of the data stated in this material data sheet is produced according to EOS Quality Management System and international standards

POWDER PROPERTIES

Powder composition is compliant with AMS5951 Rev. A Section 3.1 and UNS N07208.

Powder Chemical Composition (wt.-%)

Element	Min.	Max.
Cr	18.5	20.5
Co	9	11
Mo	8	9
Ti	1.9	2.3
Al	1.38	1.65
C	0.04	0.08
B	0.003	0.01
Ni	Balance
Mn	-	0.3
Si	-	0.15
W	-	0.5
Nb	-	0.2
Ta	-	0.1
Fe	-	1.5
Cu	-	0.1
S	-	0.015
P	-	0.015

Powder Particle Size

GENERIC PARTICLE SIZE DISTRIBUTION	20 - 55 μm

HEAT TREATMENT

Description

In as-built condition EOS NickelAlloy HAYNES® 282® has low strength and high ductility. Solution and aging heat treatments are required to produce the microstructure and strengthening phases for high temperature performance.

EOS has characterized two heat treatment options, which are described below. Heat treatment Option 1 is recommended for properties closest to wrought HAYNES® 282®.

Option 1: Recrystallization solution treatment + standard two-step aging

Option 2: Standard solution + standard two-step aging

Steps

Heat Treatment Option 1

This heat treatment results in a recrystallized microstructure with larger and more equiaxed grains than are typically found in DMLS materials. The resulting mechanical properties are isotropic, with high tensile ductility and good creep-rupture strength.

Solution treatment

Step 1: Hold at 1 250 °C (2 282 °F) for 2 hrs, followed by rapid cooling (110 °C/min (230 °F/min) or faster) to room temperature.

Aging treatment

Step 2: Hold at 1 010 °C (1 850 °F) for 2 hrs, followed by cooling equivalent to air cooling (approx 20 °C/min (68 °F/ min) or faster) to room temperature. Step 3: Hold at 788 °C (1 450 °F) for 8 hrs, followed by cooling equivalent to air cooling (approx 20 °C/min (68 °F/ min) or faster).

Heat Treatment Option 2: This heat treatment results in fine grains with high aspect ratio. Higher strength and more anisotropy may be expected relative to heat treatment Option 1.

Solution treatment

Step 1: Hold at 1 135 °C (2 075 °F) for 2 hrs, followed by rapid cooling (110 °C/min (230 °F/min) or faster) to room temperature.

Aging treatment

Step 2: Hold at 1 010 °C (1 850 °F) for 2 hrs, followed by cooling equivalent to air cooling (approx 20 °C/min (68 °F/ min) or faster) to room temperature.

Step 3: Hold at 788 °C (1 450 °F) for 8 hrs, followed by cooling equivalent to air cooling (approx 20 °C/min (68 °F/ min) or faster).